High-performance screen-printed Au/Ba0.85Sr0.15TiO3/Pt capacitors for tunable devices

Résumé

Metal-Ferroelectric-Metal capacitor structure, employing the lead free ferroelectric Ba0.85Sr0.15TiO3 thick films are successfully prepared by screen printing process on silicon platinized Pt/Ti/SiO2/Si substrates. The surface morphology and microstructure are analyzed by scanning electron microscope and X-ray diffraction. The thick film showed a well adhesion to the Pt/Ti/SiO2/Si substrate and uniform thickness of about ~ 20 µm. The frequency dependence of dielectric characteristics of BST thick films is systematically discussed and compared in a large temperature range. Ferroelectric characterizations, tunability and leakage current in the Au/BST(thick film)/Pt capacitor were also studied at room temperature by polarization cycles (P–V), Capacitance (C–V) and current (I–V) measurements. The high tunability (81%) combined with the low dielectric loss tangent and low leakage current makes Ba0.85Sr0.15TiO3 thick films one of the encouraging candidates for various modern electronic tunable devices.
Fichier principal
Vignette du fichier
S0925838821017497.pdf (2.48 Mo) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-04460074 , version 1 (22-07-2024)

Licence

Identifiants

Citer

Aymen Selmi, O. Khaldi, Manuel Mascot, F. Jomni, Jean-Claude Carru. High-performance screen-printed Au/Ba0.85Sr0.15TiO3/Pt capacitors for tunable devices. Journal of Alloys and Compounds, 2021, 878, pp.160340. ⟨10.1016/j.jallcom.2021.160340⟩. ⟨hal-04460074⟩
8 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Mastodon Facebook X LinkedIn More